Tempered Solar Glass Introduction
Solar glass is a specially developed glass for solar cell. It is made of unique formulation and high quality material whose iron content is less than 100PPM. By adopting international first-rate production technology and equipment, it has special suede and flower Solar design. This product has the characteristic of high luminousness, high stability, waterproof and high safety factor, etc.
Tempered Solar Glass Specification
Thickness: 3.2mm 4mm, 5mm, 5.5mm, 6mm etc.
Color: Ultra clear
Size: 1524*2134mm, 1650*2140mm, 1650*2440mm, 1830*2440mm, 3300*1900mm, 3210*2140mm, 3300*2134mm, 3210*2250mm, 3300*2250mm, 3660*2134mm, 3660*2250mm etc. All size can be produced according to client's request
Tempered Solar Glass Types
Low Iron Textured Glass
Low Iron Float Glass
Tempered Solar Glass Features
High light transmission, more than 91.6%
Low optical defects, comply with SPF and CE
Easily to be cut, coated and tempered
Tempered Solar Glass Application
1. Solar-cell panel
2. Solar water heater
3. Solar-powered street lamp
4. Solar energy
Features
This kind of glass has the characteristics of high solar transmittance, low absorbance, low reflectance, low iron content, high stability and high safety factor, etc.
Packing
1. Interlay paper between two sheets.
2. Seaworthy wooden crates.
3. Iron/Plastic belt for consolidation
Specification and parameter
| Standard Thickness |
3.2mm and 4mm |
| Thickness Tolerance |
3.2+-0.20mm; 4.0mm+-0.30mm; |
| Max size |
2250mm*3300mm |
| Solar Transmittance (3.2mm) |
≥ 91.6% |
| Iron Content |
≤ 120ppm Fe2O3 |
| Poisson's Ration |
0.2 |
| Density |
2.5g/CC |
| Young's Modulus |
73. Gpa |
| Tensile Strength |
42MPa |
| Hemispherical Emissivity |
0.84 |
| Epansion Coefficient |
9.03*10-6/º C |
| Softening Point |
720º C |
| Annealing Point |
550º C |